低温固化型粉末涂料

Low temperature curing powder

一般介绍:本产品是采用特殊配方和生产工艺制作的适用于中密度纤维板底材(MDF )涂装的粉末涂料,涂膜具有优异 的机械性能和户内技饰性能,可广泛用于现代家具行业的表面涂装。一般不建议直接用于各种户外用品的表面涂装。

General introduction:This type of coating is prepared from special compositions with unique production technics,and it is suitable for the coating of moderate density fibreboard(MDF)substrate. The coating films prepared from this type of coating have excellent mechanical property and indoor/outdoor decorativeness, so the powder coating can be widely used in the surface coating for modern furniture. It is suggested not to use it directly for the coating of outdoor appliances.

产品系列:现可做成多种颜色和带金属闪光效果的砂纹或锤纹类型的粉末涂料。

Product Series:The products can be turned into sand veined or hammer veined coating layers of varioucolors or with metallic flashing effect.

粉末物理性能:比重(g/cm³、25°C) :1.2-1.8

粒度分布:100%小于100微米(可根据涂装的特殊要求进行调整)

Physical properties of the powder: Density(g/cm³、25°C):1.2-1.8

Granularity distribution 100%below 100μm(it can be adapted to the customers1 demand)

固化条件120-160°C(指MDF板材表面温度),20分钟。烘炉可采用普通热风循环烘箱或烘道。条件允许的最好先用 红外线烘箱对刚喷好的涂层进行快速加热流平,再送入普通烘箱烘烤固化。

Curing Condition:120°C -160°C(surface temperature of the MDF substrate), 20 minutes. Ordinary hot-air cycling oven or drying tunnel can be used for the curing. The coating layer just sprayed had better be put in the infrared oven for the accelerated leveling if condition permitted, and then sent to ordinary ovens.

平均覆盖率:约8-9平方米/公斤,膜厚60微米(以100%的粉末涂料使用率计算)

Average coating rate : 8-9㎡/kg, film thickness:60μm(calculated according to 100% consuming of powder coating)